書誌事項
- タイトル別名
-
- Synthesis of Boron Nitride from Triammoniadecaborane and Ammonia
- トリアンモニアデカボラン ト アンモニア カラ ノ チッカ ホウソ ノ ゴウセ
この論文をさがす
抄録
Highly pure boron nitride of low crystallinity could be synthesized from triammoniadecaborane and ammonia below 800°C under atmospheric pressure. Triammoniadecaborane reacted with ammonia at temperatures between 300° and 450°C, and formed an amorphous solid containing BN, NH and BH bonds. According to the data of IR spectrum, the BH absorption band at 2500cm-1 decreased in intensity with increasing temperature, and disappeared at 800°C. The 800cm-1 band assigned to the BNB bonding increased in intensity from 700° to 800°C. The degree of alignment of the B3N3 hexagonal layer increased as the reaction time increased from 2h to 10h at 800°C. The X-ray diffraction profiles of the product formed at 800°C for 10h showed the broad diffractions centered at 2θ=25.5° and 42.0° (Cu Kα). The crystallization of boron nitride synthesized at 800°C for 10h proceeded above 1180°C. The 100 reflection of hexagonal boron nitride was separated from the broad 10 diffraction of the specimen heated at 1550°C for 2h. The lattice constant (c0) and size of crystallite (Lc) of the specimen were 6.735 and 220Å, respectively, after heating at 1550°C under atmospheric pressure for 2h. The size of crystallite increased from 320 to 830Å as the temperature increased from 1100°C to 1500°C under 2.0GPa for 10min heating. Boron nitride synthesized by heating at 800°C for 10h crystallized to hexagonal boron nitride when heated at 1500°C and 2.0GPa for 10min.
収録刊行物
-
- 窯業協會誌
-
窯業協會誌 95 (1097), 104-108, 1987
公益社団法人 日本セラミックス協会
- Tweet
キーワード
詳細情報 詳細情報について
-
- CRID
- 1390001205248558336
-
- NII論文ID
- 110002313558
-
- NII書誌ID
- AN00245650
-
- ISSN
- 18842127
- 00090255
-
- NDL書誌ID
- 3118996
-
- 本文言語コード
- ja
-
- データソース種別
-
- JaLC
- NDL
- Crossref
- CiNii Articles
-
- 抄録ライセンスフラグ
- 使用不可